Novatec LD YF30 物性表资料
低密度聚乙烯（LDPE）的应用：
LDPE适合热塑性成型加工的各种成型工艺，成型加工性好，如注塑，挤塑，吹塑，旋转成型，涂覆，发泡工艺，热成型，热封焊，热焊接等。
LDPE材料的其他牌号：
Novatec LD LJ401 LDPE Japan Polychem Corporation
Novatec LD LJ802 LDPE Japan Polychem Corporation
Novatec LD LJ803 LDPE Japan Polychem Corporation
Novatec LD LJ8041 LDPE Japan Polychem Corporation
Novatec LD LJ902 LDPE Japan Polychem Corporation
Novatec LD YF30 LDPE Japan Polychem Corporation
Novatec LD ZF33 LDPE Japan Polychem Corporation
OKITEN 222 A LDPE DIOKI d.d.
OKITEN 233 A LDPE DIOKI d.d.
OKITEN 245 A LDPE DIOKI d.d.
OKITEN 245 S LDPE DIOKI d.d.
Osterlene LD-.25-918 LDPE Osterman & Company
Osterlene LD-.7-919 LDPE Osterman & Company
Osterlene LD-1.8-921 LDPE Osterman & Company
Osterlene LD-13.5-918 LDPE Osterman & Company
加工方法 | · 薄膜挤出 | ||||||||||
物理性能 | 额定值 | 单位制 | 测试方法 | ||||||||
密度 | 0.920 | g/cm3 | ISO 1183 | ||||||||
熔流率 (190°C/2.16 kg) | 1.1 | g/10 min | ISO 1133 | ||||||||
硬度 | 额定值 | 单位制 | 测试方法 | ||||||||
支撐硬度 (邵氏 D) | 52 | ISO 868 | |||||||||
机械性能 | 额定值 | 单位制 | 测试方法 | ||||||||
拉伸应力 (断裂, 注塑) | 14.0 | MPa | ISO 527-2 | ||||||||
拉伸应变 (断裂, 注塑) | 100 | % | ISO 527-2 | ||||||||
弯曲模量 (注塑) | 130 | MPa | ISO 178 | ||||||||
冲击性能 | 额定值 | 单位制 | 测试方法 | ||||||||
简支梁缺口冲击强度 | 无断裂 | ISO 179 | |||||||||
拉伸冲击强度 | 230 | kJ/m2 | ISO 8256 | ||||||||
热性能 | 额定值 | 单位制 | 测试方法 | ||||||||
脆化温度 | -70.0 | °C | ISO 974 | ||||||||
维卡软化温度 | 91.0 | °C | ISO 306 | ||||||||
溶融温度（DSC） | 108 | °C | ISO 3146 | ||||||||
补充信息 | |||||||||||
Most properties were tested according to JIS standards. | |||||||||||
OTHER PRODUCTS
| APEX 3055 PVC |
| PP ADENE NCQA |
| 日本住友化学 PP R101 |
| AIE PA6 50G6F物性表 |
| Silicone Rubber (SIR) EL #@ UL黄卡 |
| Polyimide (PI) HJPI-50A2 UL黄卡 |
| Panlite pc AD-5503物性表 |
| RTP Compounds pc EMI 360.6 FR物性表 |
| EVA-三井聚合-560 |
Copyright © sujiaowuxing.com All Rights Reserved，