DOW LDPE 421E 物性表资料
低密度聚乙烯（LDPE）的应用：
LDPE适合热塑性成型加工的各种成型工艺，成型加工性好，如注塑，挤塑，吹塑，旋转成型，涂覆，发泡工艺，热成型，热封焊，热焊接等。
LDPE材料的其他牌号：
DOW LDPE 320E LDPE Dow Plastics
DOW LDPE 322E LDPE Dow Plastics
DOW LDPE 330E LDPE Dow Plastics
DOW LDPE 352E LDPE Dow Plastics
DOW LDPE 4005 LDPE Dow Plastics
DOW LDPE 4012 LDPE Dow Plastics
DOW LDPE 4012S LDPE Dow Plastics
DOW LDPE 401C LDPE Dow Plastics
DOW LDPE 410E LDPE Dow Plastics
DOW LDPE 410F LDPE Dow Plastics
DOW LDPE 421E LDPE Dow Plastics
物理性能 | 额定值 | 单位制 | 测试方法 | ||||||||||
比重 | 0.930 | g/cm3 | ASTM D792 | ||||||||||
熔流率 (190°C/2.16 kg) | 3.2 | g/10 min | ISO 1133 | ||||||||||
薄膜 | 额定值 | 单位制 | 测试方法 | ||||||||||
拉伸模量 | ISO 527-3 | ||||||||||||
2% 正割, MD: 50 μm | 290 | MPa | |||||||||||
2% 正割, TD: 50 μm | 250 | MPa | |||||||||||
拉伸应力 | ISO 527-3 | ||||||||||||
MD: 屈服, 50 μm | 11.0 | MPa | |||||||||||
TD: 屈服, 50 μm | 11.0 | MPa | |||||||||||
MD: 断裂, 50 μm | 19.0 | MPa | |||||||||||
TD: 断裂, 50 μm | 15.0 | MPa | |||||||||||
伸长率 | ISO 527-3 | ||||||||||||
MD: 断裂, 50 μm | 420 | % | |||||||||||
TD: 断裂, 50 μm | 550 | % | |||||||||||
落锤冲击 (50 μm) | 100 | g | ISO 7765-1/A | ||||||||||
埃尔曼多夫抗撕强度 | ASTM D1922 | ||||||||||||
MD: 50 μm | 500 | g | |||||||||||
TD: 50 μm | 350 | g | |||||||||||
热性能 | 额定值 | 单位制 | 测试方法 | ||||||||||
维卡软化温度 | 102 | °C | ASTM D1525 | ||||||||||
挤出 | 额定值 | 单位制 | |||||||||||
熔体温度 | 160 到 195 | °C | |||||||||||
挤压说明 | |||||||||||||
放大比 1:2.5 | |||||||||||||