COSMOTHENE EVA KA-31 LDPE TPC 物性表资料
低密度聚乙烯（LDPE）的应用：
LDPE适合热塑性成型加工的各种成型工艺，成型加工性好，如注塑，挤塑，吹塑，旋转成型，涂覆，发泡工艺，热成型，热封焊，热焊接等。
LDPE材料的其他牌号：
COSMOTHENE G812 LDPE TPC
COSMOTHENE G814 LDPE TPC
COSMOTHENE L420 LDPE TPC
COSMOTHENE L705 LDPE TPC
COSMOTHENE L725 LDPE TPC
COSMOTHENE EVA KA-10 LDPE TPCLtd
COSMOTHENE EVA KA-31 LDPE TPC
COSMOTHENE EVA MA-10 LDPE TPC
COSMOTHENE EVA MB-11 LDPE TPC
COTENE 2010 LDPE ICO Polymers
COTENE 2011 LDPE ICO Polymers
COTENE 2012 LDPE ICO Polymers
COTENE 2013 LDPE ICO Polymers
COTENE 2014 LDPE ICO Polymers
COTENE 2018 LDPE ICO Polymers
加工方法 | · 砑光 | |||||||||||
物理性能 | 额定值 | 单位制 | 测试方法 | |||||||||
比重 | 0.945 | g/cm3 | ASTM D792 | |||||||||
熔流率 | 7.0 | g/10 min | ASTM D1238 | |||||||||
醋酸乙烯含量 | 28.0 | wt% | ||||||||||
硬度 | 额定值 | 单位制 | 测试方法 | |||||||||
硬度计硬度 (邵氏 D) | 26 | ASTM D2240 | ||||||||||
机械性能 | 额定值 | 单位制 | 测试方法 | |||||||||
抗张强度 (屈服) | 11.8 | MPa | ASTM D638 | |||||||||
伸长率 (断裂) | 800 | % | ASTM D638 | |||||||||
热性能 | 额定值 | 单位制 | 测试方法 | |||||||||
脆化温度 | < -50.0 | °C | JIS K7216 | |||||||||
维卡软化温度 | 40.0 | °C | ASTM D1525 | |||||||||
熔融温度 | 70.0 | °C | Internal Method | |||||||||
Ring and Ball Softening Point | > 150 | ASTM E28 | ||||||||||
OTHER PRODUCTS
| PP ADENE NCTB |
| DINALON PA6 30% CM 物性表 |
| 韩国LG PP H1500 |
| 基础创新塑料(上海) PC 945 8T9D066 |
| 韩国SUHHAE TPR SR8000-60N |
| Romiloy ABS/PC 1015 物性表 |
| DIALAC ASA TW15B 物性表 |
| COC 8007S物性表资料 |
| HDPE-菲利浦石油-HHMTR160 |
Copyright © sujiaowuxing.com All Rights Reserved，