Alkathene XDS34 LDPE Qenos Pty Ltd 物性表资料
低密度聚乙烯（LDPE）的应用：
LDPE适合热塑性成型加工的各种成型工艺，成型加工性好，如注塑，挤塑，吹塑，旋转成型，涂覆，发泡工艺，热成型，热封焊，热焊接等。
LDPE材料的其他牌号：
ALCUDIA PE-063/A LDPE REPSOL YPF
ALCUDIA PE-071 LDPE REPSOL YPF
Alkathene LDF433 LDPE Qenos Pty Ltd
Alkathene XDS34 LDPE Qenos Pty Ltd
ASI POLYETHYLENE CP 763-01 Natural LDPE A. Schulman Inc.
ASI POLYETHYLENE CP 775-01 LDPE A. Schulman Inc.
ASI POLYETHYLENE CP 795-01 Natural LDPE A. Schulman Inc.
ASI POLYETHYLENE CP 831-01 LDPE A. Schulman Inc.
ASI POLYETHYLENE CP 851 LDPE A. Schulman Inc.
ASI POLYETHYLENE CP 879-01 LDPE A. Schulman Inc.
AT 190 LDPE Celanese EVA Performance Polymers
AT 191A LDPE Celanese EVA Performance Polymers
AT 193 LDPE Celanese EVA Performance Polymers
AT 214 LDPE Celanese EVA Performance Polymers
AT 220 LDPE Celanese EVA Performance Polymers
加工方法 | · 薄膜挤出 | ||||||||||||
物理性能 | 额定值 | 单位制 | 测试方法 | ||||||||||
密度 | 0.922 | g/cm3 | ASTM D1505 | ||||||||||
熔流率 (190°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238 | ||||||||||
薄膜 | 额定值 | 单位制 | 测试方法 | ||||||||||
薄膜厚度 - 经测试 | 100 | μm | |||||||||||
割线模量 | ASTM D882 | ||||||||||||
2% 正割, MD: 100 μm, 吹塑薄膜 | 130 | MPa | |||||||||||
2% 正割, TD: 100 μm, 吹塑薄膜 | 140 | MPa | |||||||||||
抗张强度 | ASTM D882 | ||||||||||||
MD: 屈服, 100 μm, 吹塑薄膜 | 11.0 | MPa | |||||||||||
TD: 屈服, 100 μm, 吹塑薄膜 | 10.0 | MPa | |||||||||||
MD: 断裂, 100 μm, 吹塑薄膜 | 26.0 | MPa | |||||||||||
TD: 断裂, 100 μm, 吹塑薄膜 | 23.0 | MPa | |||||||||||
伸长率 | ASTM D882 | ||||||||||||
MD: 断裂, 100 μm, 吹塑薄膜 | 610 | % | |||||||||||
TD: 断裂, 100 μm, 吹塑薄膜 | 820 | % | |||||||||||
落锤冲击 (100 μm, 吹塑薄膜) | 330 | g | ASTM D1709 | ||||||||||
埃尔曼多夫抗撕强度 | ASTM D1922 | ||||||||||||
MD: 100 μm, 吹塑薄膜 | 530 | g | |||||||||||
TD: 100 μm, 吹塑薄膜 | 690 | g | |||||||||||
光学性能 | 额定值 | 单位制 | 测试方法 | ||||||||||
光泽度 (45°, 100 μm, 吹塑薄膜) | 71 | ASTM D2457 | |||||||||||
雾度 (100 μm, 吹塑薄膜) | 8.0 | % | ASTM D1003 | ||||||||||
补充信息 | |||||||||||||
Film properties taken from blown film processed at a blow up ratio of 2:1. | |||||||||||||