PC/ABS C2800物性表资料
PC/ABS材料的其他牌号：
PC/ABS C2100HF
PC/ABS FR3010
PC/ABS 1800
PC/ABS C2950HF
PC/ABS MC1300
PC/ABS C2800
加工方法 | · 注射成型 | |||||||||||||||||
多点数据 | · Coefficient of Thermal Expansion vs. Temperature (ASTM E831) · Elastic Modulus vs Temperature (ASTM D4065) · Flexural DMA (ASTM D4065) · Instrumented Impact (Energy) (ASTM D3763) · Instrumented Impact (Load) (ASTM D3763) · Pressure-Volume-Temperature (PVT - Zoller Method) · Specific Heat vs. Temperature (ASTM D3417) · Tensile Creep (ASTM D2990) · Tensile Fatigue · Tensile Stress vs. Strain (ASTM D638) · Thermal Conductivity vs. Temperature (ASTM E1530) · Viscosity vs. Shear Rate (ASTM D3835) | |||||||||||||||||
物理性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
比重 | ASTM D792 | |||||||||||||||||
-- | 1.17 | g/cm3 | ||||||||||||||||
-- 3 | 1.18 | g/cm3 | ||||||||||||||||
熔流率 (260°C/2.16 kg) | 16 | g/10 min | ASTM D1238 | |||||||||||||||
收缩率 | Internal Method | |||||||||||||||||
流动: 3.20 mm | 0.40 到 0.60 | % | ||||||||||||||||
横向流动: 3.20 mm | 0.40 到 0.60 | % | ||||||||||||||||
吸水率 | ASTM D570 | |||||||||||||||||
24 hr | 0.10 | % | ||||||||||||||||
平衡, 23°C | 0.40 | % | ||||||||||||||||
硬度 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
洛氏硬度 (R 计秤) | 120 | ASTM D785 | ||||||||||||||||
机械性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
拉伸模量 4 | 2690 | MPa | ASTM D638 | |||||||||||||||
抗张强度 5 (屈服) | 58.6 | MPa | ASTM D638 | |||||||||||||||
伸长率 5 | ASTM D638 | |||||||||||||||||
屈服 | 5.0 | % | ||||||||||||||||
断裂 | 50 | % | ||||||||||||||||
弯曲模量 6 (100 mm 跨距) | 2690 | MPa | ASTM D790 | |||||||||||||||
弯曲强度 6 (屈服, 100 mm 跨距) | 96.5 | MPa | ASTM D790 | |||||||||||||||
冲击性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
悬壁梁缺口冲击强度 (23°C) | 430 | J/m | ASTM D256 | |||||||||||||||
装有测量仪表的落镖冲击 (23°C, Total Energy) | 58.3 | J | ASTM D3763 | |||||||||||||||
热性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
热变形温度 | ASTM D648 | |||||||||||||||||
1.8 MPa, 未退火, 3.20 mm | 73.9 | °C | ||||||||||||||||
1.8 MPa, 未退火, 6.40 mm | 80.0 | °C | ||||||||||||||||
维卡软化温度 | 90.6 | °C | ASTM D1525 7 | |||||||||||||||
线形膨胀系数 | ASTM E831 | |||||||||||||||||
流动: -40 到 60°C | 0.000072 | cm/cm/°C | ||||||||||||||||
横向: -40 到 60°C | 0.000072 | cm/cm/°C | ||||||||||||||||
导热系数 | 0.20 | W/m/K | ASTM C177 | |||||||||||||||
RTI Elec | 80.0 | °C | UL 746 | |||||||||||||||
RTI Imp | 70.0 | °C | UL 746 | |||||||||||||||
RTI Str | 80.0 | °C | UL 746 | |||||||||||||||
电气性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
表面电阻率 | > 1.0E+14 | ohm | ASTM D257 | |||||||||||||||
体积电阻率 | 1.0E+17 | ohm·cm | ASTM D257 | |||||||||||||||
介电强度 (3.20 mm, in Oil) | 18 | kV/mm | ASTM D149 | |||||||||||||||
介电常数 | ASTM D150 | |||||||||||||||||
50 Hz | 3.00 | |||||||||||||||||
60 Hz | 3.00 | |||||||||||||||||
100 Hz | 3.00 | |||||||||||||||||
耗散因数 | ASTM D150 | |||||||||||||||||
50 Hz | 0.0048 | |||||||||||||||||
60 Hz | 0.0048 | |||||||||||||||||
耐电弧性 8 | PLC 6 | ASTM D495 | ||||||||||||||||
相比耐漏电起痕指数(CTI) | PLC 1 | UL 746 | ||||||||||||||||
高电弧燃烧指数(HAI) | PLC 0 | UL 746 | ||||||||||||||||
高电压电弧起痕速率 (HVTR) | PLC 3 | UL 746 | ||||||||||||||||
热丝引燃 (HWI) | PLC 3 | UL 746 | ||||||||||||||||
可燃性 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
UL 阻燃等级 | UL 94 | |||||||||||||||||
0.889 mm | V-2 | |||||||||||||||||
1.47 mm | V-0 | |||||||||||||||||
2.31 mm | 5VB | |||||||||||||||||
极限氧指数 | 35 | % | ASTM D2863 | |||||||||||||||
注射 | 额定值 | 单位制 | ||||||||||||||||
干燥温度 | 77.0 到 82.0 | °C | ||||||||||||||||
干燥时间 | 3.0 到 4.0 | hr | ||||||||||||||||
干燥时间，最大 | 8.0 | hr | ||||||||||||||||
建议的最大水分含量 | 0.040 | % | ||||||||||||||||
建议注入量 | 30 到 80 | % | ||||||||||||||||
螺筒后部温度 | 210 到 254 | °C | ||||||||||||||||
螺筒中部温度 | 216 到 260 | °C | ||||||||||||||||
螺筒前部温度 | 227 到 274 | °C | ||||||||||||||||
射嘴温度 | 232 到 274 | °C | ||||||||||||||||
加工（熔体）温度 | 232 到 274 | °C | ||||||||||||||||
模具温度 | 49.0 到 71.0 | °C | ||||||||||||||||
背压 | 0.345 到 0.689 | MPa | ||||||||||||||||
螺杆转速 | 40 到 70 | rpm | ||||||||||||||||
排气孔深度 | 0.038 到 0.076 | mm | ||||||||||||||||