PBT 420物性表资料
PBT材料的其他牌号：
S650FR BK851
PBT 420se0
PBT r48
PBT 830
PBT 420
PBT 815
PBT 357u
PBT dr51
PBT 364
PBT 1731
PBT 325
加工方法 | · 注射成型 | ||||||||||||||||||||
多点数据 | · Coefficient of Thermal Expansion vs. Temperature (ASTM E831) · Elastic Modulus vs Temperature (ASTM D4065) · Flexural DMA (ASTM D4065) · Instrumented Impact (Energy) (ASTM D3763) · Instrumented Impact (Load) (ASTM D3763) · Pressure-Volume-Temperature (PVT - Zoller Method) · Shear DMA (ASTM D4065) · Specific Heat vs. Temperature (ASTM D3417) · Tensile Creep (ASTM D2990) · Tensile Fatigue · Tensile Stress vs. Strain (ASTM D638) · Thermal Conductivity vs. Temperature (ASTM E1530) · Viscosity vs. Shear Rate (ASTM D3835) | ||||||||||||||||||||
物理性能 | 额定值 | 单位制 | 测试方法 | ||||||||||||||||||
比重 | 1.53 | g/cm3 | ASTM D792 | ||||||||||||||||||
特定体积 | 0.660 | cm3/g | ASTM D792 | ||||||||||||||||||
熔流率 (250°C/2.16 kg) | 17 | g/10 min | ISO 1133 | ||||||||||||||||||
溶化体积流率（MVR） (250°C/2.16 kg) | 13.0 | cm3/10min | ISO 1133 | ||||||||||||||||||
收缩率 | Internal Method | ||||||||||||||||||||
流动 3 | 0.30 到 0.70 | % | |||||||||||||||||||
流动 4 | 0.30 到 0.50 | % | |||||||||||||||||||
流动 5 | 0.50 到 0.80 | % | |||||||||||||||||||
流动: 3.20 mm | 0.30 到 0.80 | % | |||||||||||||||||||
横向流动 3 | 0.50 到 1.0 | % | |||||||||||||||||||
横向流动 4 | 0.40 到 0.60 | % | |||||||||||||||||||
横向流动 6 | 0.60 到 0.90 | % | |||||||||||||||||||
横向流动: 3.20 mm | 0.50 到 1.0 | % | |||||||||||||||||||
吸水率 | |||||||||||||||||||||
24 hr | 0.090 | % | ASTM D570 | ||||||||||||||||||
平衡, 23°C, 50% RH | 0.080 | % | ISO 62 | ||||||||||||||||||
硬度 | 额定值 | 单位制 | 测试方法 | ||||||||||||||||||
洛氏硬度 (R 计秤) | 118 | ASTM D785, ISO 2039-2 | |||||||||||||||||||
球压硬度 (H 358/30) | 122 | MPa | ISO 2039-1 | ||||||||||||||||||
机械性能 | 额定值 | 单位制 | 测试方法 | ||||||||||||||||||
拉伸模量 | |||||||||||||||||||||
-- 7 | 9300 | MPa | ASTM D638 | ||||||||||||||||||
-- | 9300 | MPa | ISO 527-2/1 | ||||||||||||||||||
抗张强度 | |||||||||||||||||||||
屈服 8 | 120 | MPa | ASTM D638 | ||||||||||||||||||
屈服 | 125 | MPa | ISO 527-2/5 | ||||||||||||||||||
断裂 8 | 120 | MPa | ASTM D638 | ||||||||||||||||||
断裂 | 125 | MPa | ISO 527-2/5 | ||||||||||||||||||
伸长率 | |||||||||||||||||||||
屈服 8 | 2.7 | % | ASTM D638 | ||||||||||||||||||
屈服 | 2.0 | % | ISO 527-2/5 | ||||||||||||||||||
断裂 8 | 2.7 | % | ASTM D638 | ||||||||||||||||||
断裂 | 2.0 | % | ISO 527-2/5 | ||||||||||||||||||
弯曲模量 | |||||||||||||||||||||
50.0 mm 跨距 9 | 7580 | MPa | ASTM D790 | ||||||||||||||||||
-- 10 | 8500 | MPa | ISO 178 | ||||||||||||||||||
弯曲强度 | |||||||||||||||||||||
-- 10, 11 | 195 | MPa | ISO 178 | ||||||||||||||||||
屈服, 50.0 mm 跨距 9 | 195 | MPa | ASTM D790 | ||||||||||||||||||
断裂, 50.0 mm 跨距 9 | 190 | MPa | ASTM D790 | ||||||||||||||||||
抗泰伯磨耗 (1000 Cycles, 1000 g, CS-17 转轮) | 19.0 | mg | ASTM D1044 | ||||||||||||||||||
冲击性能 | 额定值 | 单位制 | 测试方法 | ||||||||||||||||||
简支梁缺口冲击强度 12 | ISO 179/1eA | ||||||||||||||||||||
-30°C | 5.0 | kJ/m2 | |||||||||||||||||||
23°C | 5.0 | kJ/m2 | |||||||||||||||||||
简支梁缺口冲击强度 12 | ISO 179/1eU | ||||||||||||||||||||
-30°C | 45 | kJ/m2 | |||||||||||||||||||
23°C | 45 | kJ/m2 | |||||||||||||||||||
悬壁梁缺口冲击强度 | |||||||||||||||||||||
-30°C | 80 | J/m | ASTM D256 | ||||||||||||||||||
23°C | 85 | J/m | ASTM D256 | ||||||||||||||||||
-30°C 13 | 7.0 | kJ/m2 | ISO 180/1A | ||||||||||||||||||
23°C 13 | 8.0 | kJ/m2 | ISO 180/1A | ||||||||||||||||||
无缺口悬臂梁冲击 | |||||||||||||||||||||
23°C | 800 | J/m | ASTM D4812 | ||||||||||||||||||
-30°C 13 | 45 | kJ/m2 | ISO 180/1U | ||||||||||||||||||
23°C 13 | 45 | kJ/m2 | ISO 180/1U | ||||||||||||||||||
装有测量仪表的落镖冲击 (23°C, Total Energy) | 8.00 | J | ASTM D3763 | ||||||||||||||||||
热性能 | 额定值 | 单位制 | 测试方法 | ||||||||||||||||||
热变形温度 | |||||||||||||||||||||
0.45 MPa, 未退火, 3.20 mm | 220 | °C | ASTM D648 | ||||||||||||||||||
0.45 MPa, 未退火, 6.40 mm | 216 | °C | ASTM D648 | ||||||||||||||||||
0.45 MPa, 未退火, 64.0 mm 跨距 14 | 217 | °C | ISO 75-2/Bf | ||||||||||||||||||
1.8 MPa, 未退火, 3.20 mm | 203 | °C | ASTM D648 | ||||||||||||||||||
1.8 MPa, 未退火, 6.40 mm | 207 | °C | ASTM D648 | ||||||||||||||||||
1.8 MPa, 未退火, 64.0 mm 跨距 14 | 204 | °C | ISO 75-2/Af | ||||||||||||||||||
维卡软化温度 | |||||||||||||||||||||
-- | 215 | °C | ASTM D1525 15, ISO 306/B50, ISO 306/B120 | ||||||||||||||||||
-- | 223 | °C | ISO 306/A50 | ||||||||||||||||||
Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |||||||||||||||||||
线形膨胀系数 | |||||||||||||||||||||
流动: -40 到 40°C | 0.000025 | cm/cm/°C | ASTM E831, ISO 11359-2 | ||||||||||||||||||
流动: 60 到 138°C | 0.000025 | cm/cm/°C | ASTM E831 | ||||||||||||||||||
横向: -40 到 40°C | 0.00012 | cm/cm/°C | ASTM E831, ISO 11359-2 | ||||||||||||||||||
导热系数 | 0.19 | W/m/K | ISO 8302 | ||||||||||||||||||
RTI Elec | 140 | °C | UL 746 | ||||||||||||||||||
RTI Imp | 140 | °C | UL 746 | ||||||||||||||||||
RTI Str | 140 | °C | UL 746 | ||||||||||||||||||
电气性能 | 额定值 | 单位制 | 测试方法 | ||||||||||||||||||
表面电阻率 | > 1.0E+15 | ohm | IEC 60093 | ||||||||||||||||||
体积电阻率 | |||||||||||||||||||||
-- | > 3.2E+16 | ohm·cm | ASTM D257 | ||||||||||||||||||
-- | > 1.0E+15 | ohm·cm | IEC 60093 | ||||||||||||||||||
介电强度 | |||||||||||||||||||||
1.60 mm, in Oil | 25 | kV/mm | ASTM D149 | ||||||||||||||||||
3.20 mm, in Air | 19 | kV/mm | ASTM D149 | ||||||||||||||||||
0.800 mm, 在油中 | 28 | kV/mm | IEC 60243-1 | ||||||||||||||||||
1.00 mm 16 | 19 | kV/mm | IEC 60243-1 | ||||||||||||||||||
1.60 mm, 在油中 | 24 | kV/mm | IEC 60243-1 | ||||||||||||||||||
3.20 mm, 在油中 | 16 | kV/mm | IEC 60243-1 | ||||||||||||||||||
介电常数 | |||||||||||||||||||||
100 Hz | 3.80 | ASTM D150 | |||||||||||||||||||
1 MHz | 3.70 | ASTM D150 | |||||||||||||||||||
50 Hz | 3.10 | IEC 60250 | |||||||||||||||||||
60 Hz | 3.10 | IEC 60250 | |||||||||||||||||||
1 MHz | 3.10 | IEC 60250 | |||||||||||||||||||
耗散因数 | |||||||||||||||||||||
100 Hz | 0.0020 | ASTM D150 | |||||||||||||||||||
1 MHz | 0.020 | ASTM D150 | |||||||||||||||||||
50 Hz | 0.0010 | IEC 60250 | |||||||||||||||||||
60 Hz | 0.0010 | IEC 60250 | |||||||||||||||||||
100 Hz | 0.0010 | IEC 60250 | |||||||||||||||||||
1 MHz | 0.010 | IEC 60250 | |||||||||||||||||||
耐电弧性 17 | PLC 5 | ASTM D495 | |||||||||||||||||||
相比耐漏电起痕指数(CTI) | PLC 0 | UL 746 | |||||||||||||||||||
漏电起痕指数 | 300 | V | IEC 60112 | ||||||||||||||||||
高电压电弧起痕速率 (HVTR) | PLC 1 | UL 746 | |||||||||||||||||||
可燃性 | 额定值 | 单位制 | 测试方法 | ||||||||||||||||||
UL 阻燃等级 (0.840 mm) | HB | UL 94 | |||||||||||||||||||
灼热丝易燃指数 (1.00 mm) | 750 | °C | IEC 60695-2-12 | ||||||||||||||||||
极限氧指数 | 19 | % | ASTM D2863 | ||||||||||||||||||
补充信息 | 额定值 | 单位制 | 测试方法 | ||||||||||||||||||
填充物 | 30 | % | ASTM D229 | ||||||||||||||||||
注射 | 额定值 | 单位制 | |||||||||||||||||||
干燥温度 | 121 | °C | |||||||||||||||||||
干燥时间 | 3.0 到 4.0 | hr | |||||||||||||||||||
干燥时间，最大 | 12 | hr | |||||||||||||||||||
建议的最大水分含量 | 0.020 | % | |||||||||||||||||||
建议注入量 | 40 到 80 | % | |||||||||||||||||||
螺筒后部温度 | 238 到 254 | °C | |||||||||||||||||||
螺筒中部温度 | 243 到 260 | °C | |||||||||||||||||||
螺筒前部温度 | 249 到 266 | °C | |||||||||||||||||||
射嘴温度 | 243 到 260 | °C | |||||||||||||||||||
加工（熔体）温度 | 249 到 266 | °C | |||||||||||||||||||
模具温度 | 65.6 到 87.8 | °C | |||||||||||||||||||
背压 | 0.345 到 0.689 | MPa | |||||||||||||||||||
螺杆转速 | 50 到 80 | rpm | |||||||||||||||||||
排气孔深度 | 0.025 到 0.038 | mm | |||||||||||||||||||